ARGOSY Aramid Paper Honeycomb Core is a kind of sandwich structure composite made of aramid paper by printing, stacking, thermal pressing, stretching, dipping, curing, slicing, and other machining processes, and by dipping in fire-resistant phenolic resin. Aramid paper has a range of
features such as:
It is available in different cell sizes such as 3.2mm, 4.0 mm, 4.8 mm, 6.4 mm, and 9.6 mm, with a density ranging from 24 kg/m³ to 144 kg/m³. It has regular cell sizes, even density, and consistent color, and its physical property, mechanical property, and fire-resistance property can meet the material standard of civil aircraft. It has passed the professional certification of the aviation industry of China. Automated production line (annual capacity 5000 m³) can produce large-sized honeycomb up to 2,440 mm(W), 1,220 mm(L), and 914 mm(H), leading the industry’s efficiency and technology.
ARGOSY Aramid Paper Honeycomb Core is widely used in:
MECHANICAL PROPERTIES OF COMMERCIAL GRADE HONEYCOMB AT ROOM TEMPERATURE
wdt_ID | PRODUCT DESCRIPTION | DATA TYPE | BARE COMP. /MPa - STRENGTH | STAB. COMP. /MPa - STRENGTH | STAB. COMP. /MPa - MOD | L SHEAR PROPERTIES /MPa - STRENGTH | L SHEAR PROPERTIES /MPa - MOD | W SHEAR PROPERTIES /MPa - STRENGTH | W SHEAR PROPERTIES /MPa - MOD |
---|---|---|---|---|---|---|---|---|---|
1 | ACCH-2-1/8-1.8 | MIN AVG. | 115 | 130 | - | 92 | 4.6 | 54 | 2.1 |
2 | MIN IND | 113 | 127 | - | 88 | 4.2 | 52 | 2.0 | |
3 | ACCH-2-1/8-1.8 | MIN AVG. | 112 | 117 | - | 89 | 4.6 | 53 | 2.4 |
4 | MIN IND. | 105 | 115 | - | 87 | 4.3 | 52 | 2.2 | |
5 | ACCH-2-1/8-1.8 | MIN AVG. | 90 | 113 | - | 89 | 4.1 | 54 | 2.4 |
6 | MIN IND. | 84 | 80 | - | 86 | 4.0 | 53 | 2.3 | |
7 | ACCH-2-1/8-3.0 | MIN AVG. | 328 | 331 | - | 190 | 7.1 | 113 | 3.9 |
8 | MIN IND. | 322 | 319 | - | 183 | 6.8 | 112 | 3.8 | |
9 | ACCH-2-1/8-3.0 | MIN AVG. | 299 | 329 | - | 189 | 7.7 | 126 | 4.8 |
10 | MIN IND. | 294 | 325 | - | 181 | 7.4 | 123 | 4.7 |